 note = {Aluminum alloy base composite castings plates with artificial holes of 2 mm in diameter were subjected to the ultrasonic measurement to verify the detectability of the casting defects near the surface of the castings. Holes at the depth of 1 mm or less were detected by the surface acoustic wave measurement, and those at the depth of 2 mm ~ 5 mm were detected by the normal incidence of the longitudinal wave. The fatigue properties of MMC were also examined by the three-point bending fatigue test, and it was found that the fatigue life of MMC was shorter than that of AC4A due to larger amount of castings defects., text, application/pdf},